GB/T 8650-2015
ActiveEvaluation of pipeline and pressure vessel steels for resistance to hydrogen-induced cracking
管线钢和压力容器钢抗氢致开裂评定方法
Application Summary AI generated
This standard specifies a test method for evaluating the resistance of pipeline and pressure vessel steels to hydrogen-induced cracking (HIC) when exposed to wet hydrogen sulfide environments. It is applied in the oil and gas industry for material qualification and quality control of steels used in sour service pipelines and pressure vessels. The standard defines specimen preparation, test solution conditions, and crack evaluation criteria to assess material suitability for environments prone to hydrogen damage.
Related Standards
GB/T 19291-2003
Corrosion of metals and alloys--General principles for corrosion testing
GB/T 19292.3-2003
Corrosion of metals and alloys--Corrosivity of atmospheres--Measurement of pollution
GB/T 19292.1-2003
Corrosion of metals and alloys--Corrosivity of atmospheres--Classification
GB/T 19292.4-2003
Corrosion of metals and alloys--Corrosivity of atmospheres--Determination of corrosion rate of standard specimens for the evaluation of corrosivity
GB/T 19292.2-2003
Corrosion of metals andalloys--Corrosivity of atmospheres--Guiding values for the corrosivity categories
GB/T 19745-2005
Corrosion tests in artificial atmosphere at very low Concentrations of polluting gas(es)
GB/T 19746-2005
Corrosion of metals and alloys-Alternate immersion test in salt solution
GB/T 19747-2005
Corrosion of metals and alloys-Determination of bimetallic Corrosion in outdoor exposure corrosion tests
Transparency note: The application summary and key sentences on this page were automatically generated by AI from the standard's original text. This content has not been human-verified and should not be used for compliance or regulatory purposes. Always refer to the official standard document from the issuing authority.